WEICON Main Catalogue Chemical and technical products Page 66
Commercial customer offer**Top sellers from Weicon
Adhesives / Sealants Technical Data RK-1300 Base Technical Sprays Colour after curing RK-7100 RK-7100 black 1:1 yellowish, transparent beige, opaque RK-7200 RK-7300 PE-PP 45 PE-PP 50 PlasticBond methyl methacrylate methyl methacrylate 1:1 1:1 1:1 1:1 1:1 10 : 1 1:1 1:1 cream white, milky cream white, milky black transparent translucent/ creamy white nearly colourless, translucent transparent cream white, milky Density of the mixture - 0.98 - 1.02 g/cm3 0.98 - 1.02 g/cm3 0.98 - 1.02 g/cm3 1.1 g/cm3 1.00 g/cm³ 1.07 g/cm³ 1.00 g/cm³ 0.98 - 1.02 g/cm3 Pot life at +20°C (+68°F) - approx. 15 Min. approx. 5 Min. approx. 5 Min. approx. 1 - 2 Min. approx. 8 Min. approx. 2 - 3 Min. approx. 6 Min. approx. 15 Min. 40,000 - 60,000 40,000 - 60,000 40,000 - 60,000 5,000 - 6,000 170,000 - 200,000 45,000 20,000 40,000 - 60,000 0.1 - 5.0 mm 0.1 - 5.0 mm 0.1 - 5.0 mm 0.1 - 2.0 mm 0.25 - 1.0 mm 0.25 - 1.0 mm 0 - 1.0 mm 0.1 - 5.0 mm -55 to +125°C (-67 to +257°F) -55 to +125°C (-67 to +257°F) -55 to +125°C (-67 to +257°F) -40 to +120°C (-40 to +248°F) -55 to +100°C (-67 to +212°F) -50 to +80°C (-58 to +176°F) -50 to +80°C (-58 to +176°F) briefly to +100°C (+212°F) -55 to +125°C (-67 to +257°F) approx. 40 min. approx. 25 min. approx. 25 min. approx. 8 min. approx. 1 h approx. 12 min. approx. 40 min. approx. 12 h approx. 60 min. approx. 24 h approx. 12 h Viscosity of the mixture (mPa.s) Adhesive gap bridging Technical Liquids RK-7000 methyl methacrylate Mixing ratio resin / hardener Temperature resistance Handling strength (35%) after Mechanical loads (50% strength) after Final strength (100%) after Assembly Pastes RK-1500 21,000 (Adhesive) 4,500 (Adhesive) max. 0.40 mm (Activator application on one side*1) max. 0.80 mm (Activator application on both sides*1) -50°C to +130°C (-58 to +266°F), briefly (30 minutes) to +180°C (+356°F) approx. 6 min. approx. 5 min. approx. 9 min. approx. 8 min. approx. 24 h Shore hardness D DIN ISO 7619 approx. 24 h - approx. 60 min. approx. 60 min. approx. 60 min. approx. 12 min. approx. 8 h 2 - 3 h (PP-PP) 6 h (Alu-Alu) 3 - 4 h (PP-PP) 24 h (Alu-Alu) 24 h (PP-PP) approx. 12 h approx. 12 h approx. 12 h approx. 6 h approx. 24 h 70 75 75 45 - 55 40 - 50 D 55 55 70 72 h (Alu-Alu) Lubricants Tensile strength DIN EN 1465: - Aluminium 20 N/mm2 (2,900 psi) 20 N/mm2 (2,900 psi) 20 N/mm2 (2,900 psi) 20 N/mm2 (2,900 psi) 20 N/mm2 (2,900 psi) 19 N/mm² (2,760 psi) 5 N/mm² (730 psi) 14 N/mm² (2,030 psi) 12 N/mm2 (1,740 psi) 20 N/mm2 (2,900 psi) - Steel 25 N/mm² (3,600 psi) 25 N/mm² (3,600 psi) 23 N/mm2 (3,300 psi) 23 N/mm2 (3,300 psi) 23 N/mm2 (3,300 psi) 22 N/mm2 (3,190 psi) 5 N/mm² (730 psi) 17 N/mm² (2,470 psi) 12 N/mm2 (1,740 psi) 23 N/mm2 (3,300 psi) - Stainless Steel 25 N/mm² (3,600 psi) 30 N/mm² (4,350 psi) 22 N/mm2 (3,190 psi) 22 N/mm2 (3,190 psi) 22 N/mm2 (3,190 psi) 27 N/mm2 (3,900 psi) 4 N/mm² (580 psi) 16 N/mm² (2,320 psi) 11 N/mm² (1,600 psi) 22 N/mm2 (3,190 psi) - PC (polycarbonate) 10 N/mm² (1,450 psi) 10 N/mm² (1,450 psi) 11 N/mm² (1,600 psi) 12 N/mm2 (1,740 psi) 12 N/mm2 (1,740 psi) 7 N/mm² (1,020 psi) 6 N/mm² (870 psi) 6 N/mm² (870 psi) 6 N/mm² (870 psi) 11 N/mm² (1,600 psi) - PMMA 9 N/mm² (1,310 psi) 8 N/mm² (1,160 psi) 9 N/mm² (1,310 psi) 9 N/mm² (1,310 psi) 9 N/mm² (1,310 psi) 4 N/mm² (580 psi) 6 N/mm² (870 psi) 7 N/mm² (1,000 psi) 8 N/mm² (1,160 psi) 9 N/mm² (1,310 psi) 6 N/mm² (900 psi) 6 N/mm² (900 psi) 7 N/mm² (1,000 psi) 7 N/mm² (1,000 psi) 7 N/mm² (1,000 psi) 7 N/mm² (1,000 psi) 8 N/mm² (1,160 psi) 11 N/mm² (1,600 psi) 3 N/mm² (440 psi) 7 N/mm² (1,000 psi) - PVC-Hart 7 N/mm² (1,000 psi) 11 N/mm² (1,600 psi) 2 12 N/mm (1,740 psi) 2 12 N/mm (1,740 psi) 2 12 N/mm (1,740 psi) 8 N/mm² (1,160 psi) 11 N/mm² (1,600 psi) 14 N/mm² (2,030 psi) 2 12 N/mm (1,740 psi) 12 N/mm2 (1,740 psi) - GFK 16 N/mm² ( 2,320 psi) 20 N/mm2 (2,900 psi) 21 N/mm2 (3,000 psi) 21 N/mm2 (3,000 psi) 21 N/mm2 (3,000 psi) 9 N/mm² (1,310 psi) 7 N/mm² (1,000 psi) 17 N/mm² (2,470 psi) 15 N/mm2 (2,200 psi) 21 N/mm2 (3,000 psi) - CFK 24 N/mm2 (3,500 psi) 27 N/mm2 (3,920 psi) 22 N/mm2 (3,190 psi) 22 N/mm2 (3,190 psi) 22 N/mm2 (3,190 psi) 12 N/mm2 (1,740 psi) 7 N/mm² (1,000 psi) 16 N/mm² (2,320 psi) 12 N/mm2 (1,740 psi) 22 N/mm2 (3,190 psi) 2 N/mm² (300 psi) 3 N/mm² (400 psi) 1 N/mm² (150 psi) 1 N/mm² (150 psi) 1 N/mm² (150 psi) 2 N/mm² (290 psi) 3 N/mm² (440 psi) 6 N/mm² (870 psi) 2 N/mm² (290 psi) 1 N/mm² (150 psi) - - - - 5 N/mm² (730 psi) 2 N/mm² (290 psi) - - - 5 N/mm² (730 psi) 7 N/mm² (1,000 psi) 12 N/mm2 (1,740 psi) - - 6 N/mm² (870 psi) 8 N/mm² (1,160 psi) 8 N/mm² (1,160 psi) - - 2 N/mm² (290 psi) - - - - - - WEICON TOOLS® - ABS - Polyamide 6.6 - POM (polyoxymethylen) - PE-HD - PP (polypropylene) - PTFE (polytetrafluorethylene) Glass transition temperature - - - - - - - - - 1 N/mm² (150 psi) Tg after curing at room temperature - -39.8 °C -40.3 °C -40.3 °C -17.5 °C 51.5 °C 46.3°C - - Tg after tempering at 120 °C - -39.5 °C -38.5 °C -38.5 °C -17.7 °C 52.4 °C 44.7°C - - - EPDM (Shore A70) Other - *1This information is dependent on the type of materials to be bonded and their respective properties. In case of porous materials or passive surfaces, such as chrome, nickel, etc. the Activator should be applied on both sides. (Bond lines of 0.15 mm to 0.25 mm in width have the highest stability). 66 Catalogue WEICON
244 Pages | Valid until 12/2025 | Previous page | Next page
Choose your language
Legal issues
The manufacturer is exclusively responsible for the content, price and article details of the products and offers presented in the catalogues. Subject to technical and optical changes by the manufacturer and errors excepted.
Request form for special products
The ToolTeam® Procurement Service
Are you looking for products that are shown in the catalogue but cannot be purchased directly online?Our procurement service will be pleased to make you a non-binding and individual offer.