WEICON Main Catalogue Chemical and technical products Page 122
Commercial customer offer**Top sellers from Weicon
Adhesives / Sealants Technical Data WEICON Adhesives and Sealants in non-cured condition Flex 310 M® HT 220+ Flex 310 M® HT 200 2-C HybridPolymer silane-modified polymer silane-modified polymer grey grey concrete-grey 250 ml 310 ml 310 ml grey white, grey stainless-steel black 290 ml 310 ml 310 ml 1.41 1.5 1.62 1.08 1.00 1.40 1.48 1.47 pasty pasty pasty pasty pasty 20.000 mPa.s solid paste pasty pasty 1 <1 <1 <1 <1 <1 self-levelling - ≤3 ≤3 +5°C to +40°C*² (+41 to +104°F) +5°C to +40°C*² (+41 to +104°F) +5°C to +40°C*² (+41 to +104°F) +5°C to +40°C*² (+41 to +104°F) +5°C to +40°C*² (+41 to +104°F) +5°C to +40°C*² (+41 to +104°F) +5°C to +40°C*² (+41 to +104°F) +5 to +35°C (+41 to +95°F) +5°C to +40°C*² (+41 to +104°F) +5°C to +40°C*² (+41 to +104°F) by humidity by humidity by humidity by humidity by humidity by humidity by humidity chemical polymerisation by humidity by humidity +5 to +40°C (+41 to +104°F) and 30% to 95% rel. humidity +5 to +40°C (+41 to +104°F) and 30% to 95% rel. humidity +5 to +40°C (+41 to +104°F) and 30% to 95% rel. humidity +5 to +40°C (+41 to +104°F) and 30% to 95% rel. humidity +5 to +40°C (+41 to +104°F) and 30% to 95% rel. humidity +5 to +40°C (+41 to +104°F) and 30% to 95% rel. humidity +5 to +40°C (+41 to +104°F) and 40% to 70% rel. humidity - +5 to +40°C (+41 to +104°F) and 30% to 95% rel. humidity +5 to +40°C (+41 to +104°F) and 30% to 95% rel. humidity 25 min. 10 min. 10 min. 10 min. 15 min. 160 min. - 13 min. 12 min. Viscosity: pasty Cure speed:*³ 1 K MS-Polymer Flex 310 M® FireSeal 290 ml 1.06 Skin-over time (minutes)*³ Flex 310 M® ProSeal grey 1.44 Curing condition: Flex 310 M® 2K 310 ml Density g/cm³: Cure type: Flex 310 M® Liquid black 1 C.-MS-Polymer 310 ml Processing temperature: Flex 310 M® Stainless-steel 1 C.-MS-Polymer 310 ml Stability/Run-off (ASTM D 2202) mm: Flex 310 M® Super-Tack 1 C. MS-Polymer transparent crystal-clear Content/Container: Technical Sprays white, grey black Colour: Technical Liquids Flex 310 M® Crystal 1 C.1 C.1 C.-MS-Polymer Polyoxypropylener Polyoxypropylener Base: Assembly Pastes Flex 310 M® Classic 10 Min. 2-3 mm in the first 2-3 mm in the first 2-3 mm in the first 24 hours 24 hours 24 hours ≥ 2,5 mm in the first 24 hours 2-3 mm in the first 2-3 mm in the first 2-3 mm in the first 24 hours 24 hours 24 hours - 2-3 mm in the first 2-3 mm in the first 24 hours 24 hours Pot life (at +23°C/+73°F and 50% rel. air humidity) - - - - - - - approx. 10 min. - Set to load bearing - - - - - - - approx. 60 min. - - Volume change (DIN EN ISO 10563) %:*³ -1 -3 - - -2 -1 - approx. 1% ≤3% ≤3% Gap filling up to max. mm: 5 5 - - 10 5 - 10 5 5 30 25 - - 40 50 12 12 12 12 18 18 40 32 26 Gap width up to max. mm: Shelf life in months: (at constant room temperature) 25 25 - - 12 12 12 12 42 40 55 - WEICON Adhesives and Sealants in cured condition Shore-A-Hardness (DIN ISO 7619): Elongation at break Lubricants 45 20 650 300 400 160 600 280 400 350 600 225 3.0 N/mm² (440 psi) 3.2 N/mm² (460 psi) 3.4 N/mm² (493 psi) 1.9 N/mm² (280 psi) 3.1 N/mm² (450 psi) 1.5 N/mm² (200 psi) 2.2 N/mm² (319 psi) 1.6 N/mm² (232 psi) 1.5 N/mm² (200 psi) Average tensile shear strength (DIN EN 1465):*4 2.1 N/mm² (300 psi) 2.0 N/mm² (290 psi) 1.8 N/mm² (260 psi) 1.6 N/mm² (232 psi) 1.5 N/mm² (218 psi) 2.5 N/mm² (360 psi) - 1.3 N/mm² (189 psi) 1.4 N/mm² (203 psi) 1.2 N/mm² (170 psi) Tear strength 20 kN/m (114 lb/in) 19 kN/m (108 lb/in) 21 kN/m (120 lb/in) - 13 kN/m (74 lb/in) 11 kN/m (63 lb/in) - - - - 15 20 - - 20 20 - - 20 20 -40°C to +90°C (120 min. 200°C; 30 min. +220°C) -40°C to +90°C (-40 to +194°F) -40°C to +90°C (-40 to +194°F) briefly (approx. 2 h) to +120°C (+248°F) -40°C to +90°C (-40 to +194°F) -40 to +90°C (-40 to +194°F) -40 to +90°C (-40 to +194°F) -40 to +90°C (-40 to +194°F) - - - - - - (DIN ISO 34): Movement absorption max. %: WEICON TOOLS® 50 3.3 N/mm² (480 psi) (DIN EN ISO 527 / 5A) %: Tensile strength of the pure adhesive/sealant (DIN EN ISO 527 / 5A): Temperature resistance: Specific forward resistance Paintable:*5 Building material category (DIN 4102): Other 57 Possible primers: -40°C to +90°C (-40 -40°C to +90°C (-40 -40°C to +90°C (-40 to +194°F) briefly to +194°F) briefly to +194°F) briefly (approx. 30 min.) to (approx. 2 h) to (approx. 2 h) to +200°C (to +392°F) +120°C (+248°F) +130°C (+266°F) 1.0 x 1010 Ω·cm 1.2 x 1012 Ω·cm 3.4 x 1011 Ω·cm only “wet-on-wet” only “wet-on-wet” only “wet-on-wet” only “wet-on-wet” only “wet-on-wet” only “wet-on-wet” only “wet-on-wet” within 3 hrs. at the within 3 hrs. at the within 3 hrs. at the within 3 hrs. at the within 3 hrs. at the within 3 hrs. at the within 3 hrs. at the latest after material latest after material latest after material latest after material latest after material latest after material latest after material application with application with application with application with application with application with application with suitable paint coating suitable paint coating suitable paint coating suitable paint coating suitable paint coating suitable paint coating suitable paint coating systems (except systems (except systems (except systems (except systems (except systems (except systems (except alkyd resin paints) alkyd resin paints) alkyd resin paints) alkyd resin paints) alkyd resin paints) alkyd resin paints) alkyd resin paints) B2 B2 B2 B2 B2 B2 B2 - B2 only “wet-on-wet” only “wet-on-wet” within 3 hrs. at the within 3 hrs. at the latest after material latest after material application with application with suitable paint coating suitable paint coating systems (except systems (except alkyd resin paints) alkyd resin paints) E (EN 13501-1) E (EN 13501-1) see primer selection see primer selection see primer selection see primer selection see primer selection see primer selection see primer selection see primer selection see primer selection see primer selection table on page 127 table on page 127 table on page 127 table on page 127 table on page 127 table on page 127 table on page 127 table on page 127 table on page 127 table on page 127 *² For easier processing, the cartridges, tubes, etc. should be heated to room temperature (+20°/+68°F) before use at low temperatures. *³ Normal climate +23°C (+73°F) and 50% relative humidity. *4 Material combination aluminium/aluminium, cleaned and degreased with Cleaner S, 1 mm layer thickness, 10 mm per minute tearing speed, fast-bond beech/beech, without pre-treatment, 1 mm layer thickness, 5 mm per minute tearing speed. *5 The WEICON One-Component Adhesives and Sealants listed above are free of substances that hinder the coating of lacquer, e.g. silicone. Thanks to the special composition, these can be painted over with suitable paint coating systems (no alkyd resin paints). However, to check the compatibility, suitability must always be determined individually in preliminary tests under the respective real-life conditions. This is essential due to the different compositions and the diversity of the substrates. The curing of the adhesives and sealants is only slightly delayed by a coating of paint. 122 Catalogue WEICON
244 Pages | Valid until 12/2025 | Previous page | Next page
Choose your language
Legal issues
The manufacturer is exclusively responsible for the content, price and article details of the products and offers presented in the catalogues. Subject to technical and optical changes by the manufacturer and errors excepted.
Request form for special products
The ToolTeam® Procurement Service
Are you looking for products that are shown in the catalogue but cannot be purchased directly online?Our procurement service will be pleased to make you a non-binding and individual offer.