TECHNICAL FEATURES Properties Standard XEPOX P XEPOX L XEPOX F XEPOX D XEPOX G Density ASTM D 792-66 ≈ 1,10 ≈ 1,40 ≈ 1,45 ≈ 2,00 ≈ 1,90 Stoichiometric volume ratio (A/B)(1) - 100 : 50 (2) 100 : 50 100 : 50 100 : 50 100 : 50 Pot life 23 ± 2° 150 cc ERL 13-70 [min] - 50 ÷ 60 50 ÷ 60 50 ÷ 60 60 ÷ 70 Working life of the mixture ERL 13-70 [min] 25 ÷ 30 25 ÷ 30 25 ÷ 30 25 ÷ 30 - Application temperature (maximum relative moisture 90%) - [°C] 10 ÷ 35 10 ÷ 35 10 ÷ 35 5 ÷ 40 5 ÷ 40 Suggested thickness - [mm] 0 .1 ÷ 2 1÷2 2÷4 2÷6 1 ÷ 10 Normal adhesion tension σ EN 12188 [N/mm2] 21 27 25 19 23 Slant shear strength σ 0 50° EN 12188 [N/mm2] 94 70 93 55 102 Slant shear strength σ 0 60° EN 12188 [N/mm2] 106 88 101 80 109 Slant shear strength σ 0 70° EN 12188 [N/mm2] 121 103 115 95 116 Shear-adhesion strength τ EN 12188 [N/mm2] 39 27 36 27 37 Unitary breaking load in compression(3) EN 13412 [N/mm2] 83 88 85 84 94 EN 13412 [N/mm2] 3438 3098 3937 3824 5764 Thermal expansion coefficient (ranging between -20°C / +40°C) EN 177 [m/m∙°C] 7,0 x 10-5 7,0 x 10-5 6,0 x 10-5 6,0 x 10-5 7,0 x 10-5 Tensile strength(4) ASTM D638 [N/mm2] 40 36 30 28 30 Elastic modulus in tension(4) ASTM D638 [N/mm2] 3300 4600 4600 6600 7900 Flexural strength(4) ASTM D790 [N/mm2] 86 64 38 46 46 Elastic modulus in flexure(4) ASTM D790 [N/mm2] 2400 3700 2600 5400 5400 Unitary shear strength by punch tool(4) ASTM D732 [N/mm2] 28 28 28 19 25 Viscosity - [mPa∙s] A = 1100 B = 250 A = 2300 B = 800 A = 14000 B = 11500 Elastic modulus in compression A = 300000 A = 450000 B = 300000 B = 13000 NOTES: (1) The components are packaged in pre-measured quantities, ready to use . The ratio is by volume (not weight) . (2) It is best not to use more than one litre of mixed product at a time . The weight ratio between components A:B is around 100:44,4 . (3) Average value at the end of the loading / unloading cycles . (4) Test values from the research campaign “Innovative links for timber structural elements” - Politecnico di Milano . EPOXY ADHESIVES AND HOOKED PLATES | XEPOX | 149
576 Pages | Valid until 04/2024 | Previous page | Next page
Choose your language
Legal issues
The manufacturer is exclusively responsible for the content, price and article details of the products and offers presented in the catalogues. Subject to technical and optical changes by the manufacturer and errors excepted.
Request form for special products
The ToolTeam® Procurement Service
Are you looking for products that are shown in the catalogue but cannot be purchased directly online?Our procurement service will be pleased to make you a non-binding and individual offer.